Effects of manufacturing parameters on Performance Teak decay Parties enhanced with Polyethylene Films
Abstract
Flexible decorative veneers. made by low temperature plasma treatment. improve.Interface ~ teak veneers, low density polyethylene (LDPE) films. veneers, films. then joined by hot-pressing.
Showed, peel, transverse tensile. most significantly impacted by hot pressing temperature followed by Plasma processing speed. Optimal technology. making. veneers. 0.8 MPa. hot-pressing pressure 135℃. Temperature150 s. pressure time, 3 m/min. plasma processing speed. 0.51 kN/m. peel 4.13 MPa. transverse tensile, good flexibility. veneers. achieved. above manufacturing parameters.
Keywords
Full Text:
PDFReferences
Zhang zhankuan, Peng xiaorui, Zhang Devin. One Kind of Flexible Composite Thin wood and its processing method: China Zl201410013628.5 [p]. 2016-08-1 7.
Zeng Zhigao. Study on Manufacturing Technology and Application Technology of flexible decorative thin wood[D]Nanjing: Nanjing Forestry University, 2003: 1-31.
Peng xiaorui, Zhang zhankuanPresent Situation and Development of flexible Decorative VeneerExhibition[J]. Timber Industry, 2016, 30 (6): 23-26.
Kim B s, B h c Hun lee w I, et al. Effect of plasm a treatment on Wood Flour for wood flour/PP Co posites [J]. journa L of thermoplastic composite mate Ries, 2009, 22 (1): 21-28.
Peng xiaorui, Zhang zhankuan.Study on the Preparation, process and performance of Plastic Film Reinforced flexibility and Decorative Veneer[J]. Timber Industry, 2017, 31 (1): 50-53.
Peng xiaorui, Zhang zhankuan.Preparation of plastic film reinforced flexible decorative veneer by Plasma Modification[J]. Timber Industry, 2017, 31 (3): 49-53.
Rao Limin, Li Yile, Zhang Hongjian.Effects of teak benzene alcohol extracts on Birch WoodMUFEffects of gluing Effect[J].Western Forestry Science, 2 10, 39 (2): 42-45.
Peng xiaorui.Study on the Preparation and Properties of plasma modified polyethylene membrane reinforced flexible decorative thin wood[D].Beijing: Chinese Academy of Forestry,2017.
Fang L Chang L [w j et al. influence. silane surface modification. veneer. interfacial adhesion. wood-plastic Plywood [J]. applied Surface Science, 2014 (288): 682-689.
Wolkenhauer A militz h vi o l W. increased PVA-glue adhesion. particle board, fiber board by plasma treatment [J]. european Journ Al. Wood, Wood Products 2008 66 (2): 143-145.
Wolkenhauer A avramidis G Ha uswald e et al. plasma treatment o f wood-Plastic CO mposites. enhance. adhesion PR operties [J]. journ Al. adhesion Science, technolo gy 2008 22 (16): 2025-2037.
Aydin I. activation. wood surf aces. glue Bo NDS by mechanica l pre-treatment, its effects. some properties. veneer surfaces, plywood panels [J]. applied Surfac e science 2004 2 33 (1-4): 268-274.
Refbacks
- There are currently no refbacks.